Температура стеклования
Температура стеклования for 68 materials. The figures are taken from the property tables of the material pages and change with them; the link in each row leads to that row of the material's table.
| Material | Value | Conditions | Standard, note |
|---|---|---|---|
| AKSOPEEK®in table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| AKSOPEEK® CFin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| AKSOPEEK® HAin table | 146 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| AKSOPEEK® LCFin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6in table | 45 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6 BKin table | 45 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6 GFin table | 49 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6 MOin table | 51 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6Cin table | 40 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6C BKin table | 40 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6C Lin table | 48 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6C L BKin table | 42 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6C L YWin table | 42 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6C MCin table | 49 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA6C MOin table | 43 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA66in table | 47 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA66 BKin table | 47 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA66 GFin table | 48 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PA66 MOin table | 52 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PAIin table | 275 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PAI CF30in table | 275 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PAI GFin table | 275 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PCin table | 149 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PC BKin table | 240 °C | ||
| PCTFEin table | 45 °C | Tg | DSC |
| PE-HDin table | -110 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PE-HD BKin table | -110 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PE-HMWin table | -95 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEKin table | 150 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK BKin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK BLUEin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK CFin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK Ein table | 150 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK GFin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK GQin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK PVXin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK SWRin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK TFin table | 140 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK-CF-LFin table | 143 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEEK-LCFin table | 147 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEIin table | 216 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEI BKin table | 216 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PEI GFin table | 216 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PESin table | 225 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PETin table | 81 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PET BKin table | 81 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PET TFin table | 82 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PI PVXin table | 353 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PMMAin table | 106 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| POM ELSin table | -60 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| POM-Cin table | -60 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| POM-C BKin table | -60 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| POM-C coloredin table | -60 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| POM-Hin table | -60 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| POM-H BKin table | -60 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| POM-H TFin table | -60 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PP-Hin table | -10 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PPSin table | 97 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PPS BKin table | 97 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PPS GFin table | 93 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PPS GF BKin table | 93 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PPSUin table | 218 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PPSU BKin table | 218 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PPSU BUin table | 218 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PSUin table | 185 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PTFEin table | -120 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PTFE KFin table | -120 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |
| PVDFin table | -40 °C | Tg | ГОСТ Р 55135-2012 (ISO 11357-2:1999) |